Efficacy of 30% and 38% Silver Diamine Fluoride in Arresting Caries Lesions After Different Application Times: An in Vitro Study

Abstract Objective: To evaluate the efficacy of silver diamine fluoride (SDF) in arresting dentin caries lesions when applied under different concentrations and times. Material and Methods: Forty-two bovine blocks were selected and fixed in 24-well plates. Each well received a mixed bacterial inoculum added to the culture medium with 5% sucrose. The plates were incubated in microaerophilia (7 days) for caries formation, confirmed by micro-CT (M1). SDF was applied over the carious lesions for different times and concentrations (n=6): SDF 30% - immediate removal, 1 minute and 3 minutes; SDF 38%, - immediate removal, 1 minute and 3 minutes. The group without treatment was the control. Then, the samples were again scanned by micro-CT (M2) and submitted to a second cariogenic challenge for 21 days. Then, a final scan was performed (M3). Results: Mean pH at the culture medium and lesion depth were compared using Kruskal-Wallis and Wilcoxon tests. 38% SDF showed the lowest metabolic activity of the biofilm. All 38% groups and 30% 1 and 3 minutes did not show an increase in mean lesion depth comparing M3 with M1. However, only 30% 3 minutes and 38% 1 and 3 minutes showed a significant reduction of lesion depth. Conclusion: The minimum application time of 30% SDF to arrest dentin caries lesion was 1 minute, while 38% SDF arrested with application and immediate removal.

In vitro effect of experimental nanocomposites solutions on the prevention of dental caries around orthodontic brackets

Abstract This study aimed to evaluate the in vitro effect of a single application of experimental nanocomposite solutions on the prevention of dental caries around orthodontic brackets. The specimens were exposed to mesoporous silica (MS) nanocomposites containing fluoride by association with titanium tetrafluoride (TiF4) or sodium fluoride (NaF). Nanocomposites also could contain calcium and groups were described as MSCaTiF4, MSTiF4, MSCaNaF, MSNaF, and controls (TiF4, and NaF). Specimens were subjected to the formation of a multispecies biofilm to generate a cariogenic challenge. After 24h, both pH and total soluble fluoride concentration of the culture medium were assessed. Mineral loss was evaluated by percentage of surface mineral loss (%SML), mineral volume variation (ΔZ) of inner enamel and polarized light microscopy (PL). Linear (Ra) and volumetric (Sa) surface roughness and scanning electronic microscopy (SEM) were used to assess enamel topography. Statistical analyses were conducted considering p<0.05. MSNaF had the highest value of culture medium pH after cariogenic challenge, similarly to MSTiF4. All nanocomposite solutions released less fluoride than their controls NaF and TiF4 (p<0.05). All nanocomposite solutions presented lower %SML compared to their respective control groups (p<0.05). Lower Ra, Sa and ΔZ were observed for experimental groups compared to TiF4 (p<0.05). The results were confirmed by PL and SEM analysis. The experimental nanocomposite solutions contributed for lower enamel demineralization around orthodontic brackets.

RESUMO Este estudo teve como objetivo avaliar o efeito in vitro de uma única aplicação de soluções experimentais de nanocompósitos na prevenção de cárie dentária em braquetes ortodônticos. Os espécimes foram expostos a nanocompósitos de sílica mesoporosa (MS) contendo fluoreto por associação com tetrafluoreto de titânio (TiF4) ou fluoreto de sódio (NaF). Os nanocompósitos também podem conter cálcio e os grupos foram descritos como MSCaTiF4, MSTiF4, MSCaNaF, MSNaF e controles (TiF4 e NaF). Os espécimes foram submetidos à formação de um biofilme multiespécie para gerar um desafio cariogênico. Após 24h, o pH e a concentração de flúor solúvel total do meio de cultura foram avaliados. A perda mineral foi avaliada pela porcentagem de perda mineral superficial (% SML), variação do volume mineral (ΔZ) do esmalte interno e microscopia de luz polarizada (PL). A rugosidade superficial linear (Ra) e volumétrica (Sa) e a microscopia eletrônica de varredura (MEV) foram utilizadas para avaliar a topografia do esmalte. As análises estatísticas foram realizadas considerando p <0,05. MSNaF apresentou o maior valor de pH do meio de cultura após o desafio cariogênico, semelhante ao MSTiF4. Todas as soluções de nanocompósitos liberaram menos flúor do que seus controles NaF e TiF4 (p <0,05). Todas as soluções de nanocompósitos apresentaram% SML menor em comparação com seus respectivos grupos de controle (p <0,05). Ra, Sa e ΔZ menores foram observados para os grupos experimentais em comparação ao TiF4 (p <0,05). Os resultados foram confirmados por análises PL e SEM. As soluções experimentais de nanocompósitos contribuíram para a menor desmineralização do esmalte ao redor dos braquetes ortodônticos.